Hot Rolled STAINLESS Stol Blat Plack
Produkt beschreiwung
| Material Liwwerung: | ||||||||||||
| ASTM/ASME | EN Grad | Chemeschen Komponent % | ||||||||||
| C | Cr | Ni | Mn | P | S | Mo | Si | Cu | N | Aner | ||
| 201 |
| ≤0,15 | 16.00-18.00 Uhr | 3.50-5.50 | 5,50-7,50 | ≤0,060 | ≤0,030 | - | ≤1.00 | - | ≤0,25 | - |
| 301 | 1.4310 | ≤0,15 | 16.00-18.00 Uhr | 6.00-8.00 | ≤2.00 | ≤0,045 | ≤0,030 | - | ≤1.00 | - | 0.1 | - |
| 304 | 1.4301 | ≤0,08 | 18.00-20.00 Uhr | 8.00-10.00 | ≤2.00 | ≤0,045 | ≤0,030 | - | ≤0,75 | - | - | - |
| 304l | 1.4307 | ≤0,030 | 18.00-20.00 Uhr | 8.00-10.00 | ≤2.00 | ≤0,045 | ≤0,030 | - | ≤0,75 | - | - | - |
| 304H | 1.4948 | 0.04~0.10 | 18.00-20.00 Uhr | 8.00-10.00 | ≤2.00 | ≤0,045 | ≤0,030 | - | ≤0,75 | - | - | - |
| 309S | 1.4828 | ≤0,08 | 22.00-24.00 Uhr | 12.00-15.00 Uhr | ≤2.00 | ≤0,045 | ≤0,030 | - | ≤0,75 | - | - | - |
| 309 H |
| 0.04~0.10 | 22.00-24.00 Uhr | 12.00-15.00 Uhr | ≤2.00 | ≤0,045 | ≤0,030 | - | ≤0,75 | - | - | - |
| 310S | 1.4842 | ≤0,08 | 24.00-26.00 Uhr | 19.00-22.00 Uhr | ≤2.00 | ≤0,045 | ≤0,030 | - | ≤1,5 | - | - | - |
| 310 H | 1.4821 | 0.04~0.10 | 24.00-26.00 Uhr | 19.00-22.00 Uhr | ≤2.00 | ≤0,045 | ≤0,030 | - | ≤1,5 | - | - | - |
| 316 | 1.4401 | ≤0,08 | 16.00-18.50 Uhr | 10.00-14.00 | ≤2.00 | ≤0,045 | ≤0,030 | 2.00-3.00 | ≤0,75 | - | - | - |
| 316l | 1.4404 | ≤0,030 | 16.00-18.00 Uhr | 10.00-14.00 | ≤2.00 | ≤0,045 | ≤0,030 | 2.00-3.00 | ≤0,75 | - | - | - |
| 316 H |
| 0.04~0.10 | 16.00-18.00 Uhr | 10.00-14.00 | ≤2.00 | ≤0,045 | ≤0,030 | 2.00-3.00 | ≤0,75 | - | 0.10-0.22 | - |
| 316 Ti | 1.4571 | ≤0,08 | 16.00-18.50 Uhr | 10.00-14.00 | ≤2.00 | ≤0,045 | ≤0,030 | 2.00-3.00 | ≤0,75 | - | - | Ti5(C+N)~0,7 |
| 317l | 1.4438 | ≤0,03 | 18.00-20.00 Uhr | 11.00-15.00 Uhr | ≤2.00 | ≤0,045 | ≤0,030 | 3.00-4.00 | ≤0,75 | - | 0.1 | - |
| 321 | 1.4541 | ≤0,08 | 17.00-19.00 Uhr | 9.00-12.00 | ≤2.00 | ≤0,045 | ≤0,030 | - | ≤0,75 | - | 0.1 | Ti5(C+N)~0,7 |
| 321 H | 1.494 | 0.04~0.10 | 17.00-19.00 Uhr | 9.00-12.00 | ≤2.00 | ≤0,045 | ≤0,030 | - | ≤0,75 | - | 0.1 | Ti4(C+N)~0,7 |
| 347 | 1.4550 | ≤0,08 | 17.00-19.00 Uhr | 9.00-13.00 | ≤2.00 | ≤0,045 | ≤0,030 | - | ≤0,75 | - | - | Nb≥10*C%-1,0 |
| 347 H | 1.4942 | 0.04~0.10 | 17.00-19.00 Uhr | 9.00-13.00 | ≤2.00 | ≤0,045 | ≤0,030 | - | ≤0,75 | - | - | Nb≥8*C%-1,0 |
| 409 | S40900 | ≤0,03 | 10.50-11.70 | 0,5 | ≤1.00 | ≤0,040 | ≤0,020 | - | ≤1.00 | - | 0,03 | Ti6(C+N) -0,5 Nb0,17 |
| 410 | 1 kr13 | 0,08~0,15 | 11.50-13.50 Uhr | - | ≤1.00 | ≤0,040 | ≤0,030 | - | ≤1.00 | - | - | - |
| 420 | 2 kr13 | ≥0,15 | 12.00-14.00 Uhr | - | ≤1.00 | ≤0,040 | ≤0,030 | - | ≤1.00 | - | - | - |
| 430 | S43000 | ≤0,12 | 16.00-18.00 Uhr | 0,75 | ≤1.00 | ≤0,040 | ≤0,030 | - | ≤1.00 | - | - | - |
| 431 | 1Cr17Ni2 | ≤0.2 | 15.00-17.00 Uhr | 1.25-2.50 | ≤1.00 | ≤0,040 | ≤0,030 | - | ≤1.00 | - | - | - |
| 440 C | 11 Kr17 | 0,95-1,20 | 16.00-18.00 Uhr | - | ≤1.00 | ≤0,040 | ≤0,030 | 0,75 | ≤1.00 | - | - | - |
| 17-4PH | 630/1.4542 | ≤0,07 | 15.50-17.50 Uhr | 3.00-5.00 | ≤1.00 | ≤0,040 | ≤0,030 | - | ≤1.00 | 3.00-5.00 | - | Nb+Ta: 0,15-0,45 |
| 17-7 Uhr u | 631 | ≤0,09 | 16.00-18.00 Uhr | 6.50-7.50 | ≤1.00 | ≤0,040 | ≤0,030 | - | ≤1.00 | - | - | Al 0,75-1,50 |
| Gréisst Fourniture: | ||||||
| 3 | 3*1000*2000 | 3*1219*2438 | 3*1500*3000 | 3*1500*6000 | ||
| 4 | 4*1000*2000 | 4*1219*2438 | 4*1500*3000 | 4*1500*6000 | ||
| 5 | 5*1000*2000 | 5*1219*2438 | 5*1500*3000 | 5*1500*6000 | ||
| 6 | 6*1000*2000 | 6*1219*2438 | 6*1500*3000 | 6*1500*6000 | ||
| 7 | 7*1000*2000 | 7*1219*2438 | 7*1500*3000 | 7*1500*6000 | ||
| 8 | 8*1000*2000 | 8*1219*2438 | 8*1500*3000 | 8*1500*6000 | ||
| 9 | 9*1000*2000 | 9*1219*2438 | 9*1500*3000 | 9*1500*6000 | ||
| 10.0 | 10*1000*2000 | 10*1219*2438 | 10*1500*3000 | 10*1500*6000 | ||
| 12.0 | 12*1000*2000 | 12*1219*2438 | 12*1500*3000 | 12*1500*6000 | ||
| 14.0 | 14 * 1000 * 2000 | 14*1219*2438 | 14 * 1500 * 3000 | 14*1500*6000 | ||
| 16.0 | 16 * 1000 * 2000 | 16*1219*2438 | 14 * 1500 * 3000 | 14*1500*6000 | ||
| 18.0 | 18*1000*2000 | 18*1219*2438 | 18*1500*3000 | 18*1500*6000 | ||
| 20 | 20*1000*2000 | 20*1219*2438 | 20*1500*3000 | 20*1500*6000 |